Fabrication of MgB₂ monofilament wire by in-situ using powder-in-tube (PIT) method

In this research we have studied the making of MgB₂ superconducting monofilament wire using powder-in-tube method with variation of Mg composition to B ie 0.90, 1.00 and 1.10, while Boron remains The precursor used is Mg powder (98%) and powder B (95%) Both materials are mixed and then crushed with agate mortar for 30 minutes and then put into stainless steel tube 316. The tube is then subjected to a mechanical treatment of rolling to form its monofilament wire. The wire is then cut and sintered at a temperature of 800^o C for 2 hours. After that we measure the critical temperature then characterize the samples by XRD and SEM. From the result of this research it was found that in-situ wire-making by powder-in-tube method can make MgB₂ superconducting monofilament wire with MgB₂ as the dominant phase around 95% and MgO as the impurity phase around 5%. MgO is formed due to the oxidation occurring in the MgB₂ powder inside the wire. The optimal Mg:B composition to make this wire is in the 1:2 composition Because it has a good resistivity curve with a high enough Tc Onset that is 41,67 K and Tc Zero 40,89 K. However, there is a porosity in the wire due to the volume reduction of the Mg + 2B reaction plus the evaporation of Mg.