TY - JOUR
T1 - Synthesis zeolite y from kaolin bangka belitung
T2 - 6th International Conference on Mathematics, Science, and Education, ICMSE 2019
AU - Safitri, L. E.
AU - Zuryati, U. K.
AU - Rohma, H. N.
AU - Ni'Mah, Y. L.
AU - Prasetyoko, D.
N1 - Publisher Copyright:
© Published under licence by IOP Publishing Ltd.
PY - 2020/7/3
Y1 - 2020/7/3
N2 - Zeolite Y has been synthesized from Kaolin Bangka Belitung as precursor through activation of metakaolin with acid. The synthesis of zeolite Y consist of metakaolinitation, activation metakaolin with sulfuric acid using various concentrations (3, 6, 9, 12, and 15 M), aging, hydrothermal process for 24 hours at 100 ?C. The solid products were characterized with X-ray Diffraction (XRD), Infrared Spectroscopy (FTIR), and Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX). The result of XRD and FTIR indicated that zeolite Y formed at the variations 3, 6, 9, 12, and 15M. Based on XRD pattern of the results, phase of zeolite P formed at the variation 3M. The surface morphology and ratio of Si/Al of Zeolite Y was analyzed using SEM-EDX. The SEM micrograph of zeolite Y and P with variation of sulfuric acid 3, 6, 9, 12, and 15M like octahedral and sphere form and the ratio of Si/Al of the products based on EDX are 1.7; 1.6; 1.58; 1.64; and 1.59 respectively.
AB - Zeolite Y has been synthesized from Kaolin Bangka Belitung as precursor through activation of metakaolin with acid. The synthesis of zeolite Y consist of metakaolinitation, activation metakaolin with sulfuric acid using various concentrations (3, 6, 9, 12, and 15 M), aging, hydrothermal process for 24 hours at 100 ?C. The solid products were characterized with X-ray Diffraction (XRD), Infrared Spectroscopy (FTIR), and Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX). The result of XRD and FTIR indicated that zeolite Y formed at the variations 3, 6, 9, 12, and 15M. Based on XRD pattern of the results, phase of zeolite P formed at the variation 3M. The surface morphology and ratio of Si/Al of Zeolite Y was analyzed using SEM-EDX. The SEM micrograph of zeolite Y and P with variation of sulfuric acid 3, 6, 9, 12, and 15M like octahedral and sphere form and the ratio of Si/Al of the products based on EDX are 1.7; 1.6; 1.58; 1.64; and 1.59 respectively.
UR - http://www.scopus.com/inward/record.url?scp=85087909991&partnerID=8YFLogxK
U2 - 10.1088/1742-6596/1567/3/032099
DO - 10.1088/1742-6596/1567/3/032099
M3 - Conference article
AN - SCOPUS:85087909991
SN - 1742-6588
VL - 1567
JO - Journal of Physics: Conference Series
JF - Journal of Physics: Conference Series
IS - 3
M1 - 032099
Y2 - 9 October 2019 through 10 October 2019